Standard: | JIS, GB, DIN, BS, ASTM, AISI |
---|---|
Application: | Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard |
Material: | Steel |
Type: | Wear Resistant Plate |
Transport Package: | Steel Frame or as Required Package |
Specification: | 3+3, 6+4, 8+6, 10+12, 12+12, etc |
Customization: |
---|
Suppliers with verified business licenses
Our Wear plate has following advantages:
1. Flat surface and nice outlooking 2. Outstanding welding strength
3. Excellent wear resistance 4. Excellent impact resistance
5. Easy processing 6. High Cost Performance
7. Comprehensive quality control.
Other Feature and Property
I. Product mold introduction
*WD100 (Low stress abrasive wear)
WD100bimetal wear resistant composite steel plate is suitable for the low stress, little impact abrasive wear or fine particles, minimal energy and small incident Angle erosion wear condition.
Hard-facing layer main chemical composition of metal (Wt%)
C |
Cr |
B |
Other |
3~5 |
20~28 |
+ |
4~8 |
Hard-facing layer hardness: 60-65HRC
Wear resistant temperature: <500ºC
*WD200 (Resistance to medium impact abrasive wear)
WD200 bimetal wear resistant composite steel plate is suitable for the medium impact abrasive wear or rolling compaction wear condition under high pressure.
Hard-facing layer main chemical composition of metal (Wt%)
C |
Cr |
Mo |
Mn |
Other |
2~5 |
20~26 |
+ |
1~3 |
2~5 |
Hard-facing layer hardness: >58HRC
Wear resistant temperature: <500ºC
*WD300 (Resistance to high temperature abrasive wear)
HP300 bimetal wear resistant composite steel plate is suitable for high temperature abrasive wear and fine particles, small Angle, small energy impact wear conditions.
Hard-facing layer main chemical composition of metal (Wt%)
C |
Cr |
Nb |
Mn |
Other |
4~6 |
18~24 |
5~8 |
2~3 |
3~6 |
Hard-facing layer hardness: 60-68HRC
Wear resistant temperature: <800ºC
*WD400 (Resistance to strong impact abrasive wear)
WD400 bimetal wear resistant composite steel plate is suitable for high stress, strong impact conditions.
Hard-facing layer main chemical composition of metal (Wt%)
C |
Cr |
Mn |
Other |
0.4~1.5 |
3~7 |
15~22 |
2~5 |
Hard-facing layer hardness: 20-25HRC (normal condition), 50-55HRC (after cold and rigidification)
Wear resistant temperature: <500ºC
Flatness tolerance: Flatness tolerance is ±3mm/m.
Thickness tolerance: Uniform overlay thickness, with tolerance within 0-0.3mm.
Product Name | Wear Resistant Hardfacing Steel Plate |
Material | High chrome, high carbon alloy |
Welding Wire | VAUTID 100 |
Thickness | 6+4 , 6+6, 8+4, 8+6, 10+8,10+10, 12+12 etc |
Hardness | HRC 58-62 |
Technical | Open Arc Welding |
Operating temperature | Up to 350 degrees |
Wear Resistance | Wear Resistance |
Impact resistance | Medium |
Microstructure | Mixture of high volume hexagonal shaped chromium carbides in tough austenitic and martensitic matrix |
Wear Testing | ASTM G65 |
Cracks | Visible cracks on the surface are formed for releasing stress |
Fabrication | Cutting, Machining, Bending, Welding |
Application | Mining,Steel,Cement,Power,Port,etc |